Bacterial Adhesion and Surface Roughness for Different Clinical Techniques for Acrylic Polymethyl Methacrylate.

This study sought to assess the effect of different surface finishing and polishing protocols on the surface roughness and bacterial adhesion (S. sanguinis) to polymethyl methacrylates (PMMA). Fifty specimens were divided into 5 groups (n = 10) according to their fabrication method and surface finishing protocol: LP (3 : 1 ratio and laboratory polishing), NF (Nealon technique and finishing), NP (Nealon technique and manual polishing), MF (3 : 1 ratio and manual finishing), and MP (3 : 1 ratio and manual polishing). For each group, five specimens were submitted to bacterial adhesion tests and analyzed by scanning electron microscopy (SEM). Two additional specimens were subjected to surface topography analysis by SEM and the remaining three specimens were subjected to surface roughness measurements. Data were compared by one-way ANOVA. The mean bacterial counts were as follows: NF, 19.6 ± 3.05; MP, 5.36 ± 2.08; NP, 4.96 ± 1.93; MF, 7.36 ± 2.45; and LP, 1.56 ± 0.62 (CFU). The mean surface roughness values were as follows: NF, 3.23 ± 0.15; MP, 0.52 ± 0.05; NP, 0.60 ± 0.08; MF, 2.69 ± 0.12; and LP, 0.07 ± 0.02 (µm). A reduction in the surface roughness was observed to be directly related to a decrease in bacterial adhesion. It was verified that the laboratory processing of PMMA might decrease the surface roughness and consequently the adhesion of S. sanguinis to this material.

Influence of core-finishing intervals on tensile strength of cast posts-and-cores luted with zinc phosphate cement

The core finishing of cast posts-and-cores after luting is routine in dental practice. However, the effects of the vibrations produced by the rotary cutting instruments over the luting cements are not well-documented. This study evaluated the influence of the time intervals that elapsed between the cementation and the core-finishing procedures on the tensile strength of cast posts-and-cores luted with zinc phosphate cement. Forty-eight bovine incisor roots were selected, endodontically treated, and divided into four groups (n = 12): GA, control (without finishing); GB, GC, and GD, subjected to finishing at 20 minutes, 60 minutes, and 24 hours after cementation, respectively. Root canals were molded, and the resin patterns were cast in copper-aluminum alloy. Cast posts-and-cores were luted with zinc phosphate cement, and the core-finishing procedures were applied according to the groups. The tensile tests were performed at a crosshead speed of 0.5 mm/min for all groups, 24 hours after the core-finishing procedures. The data were subjected to one-way analysis of variance (ANOVA) and Tukey's test (α = 0.05). No significant differences were observed in the tensile strengths between the control and experimental groups, regardless of the time interval that elapsed between the luting and finishing steps. Within the limitations of the present study, it was demonstrated that the core-finishing procedures and time intervals that elapsed after luting did not appear to affect the retention of cast posts-and-cores when zinc phosphate cement was used.

Influence of core-finishing intervals on tensile strength of cast posts-and-cores luted with zinc phosphate cement.

The core finishing of cast posts-and-cores after luting is routine in dental practice. However, the effects of the vibrations produced by the rotary cutting instruments over the luting cements are not well-documented. This study evaluated the influence of the time intervals that elapsed between the cementation and the core-finishing procedures on the tensile strength of cast posts-and-cores luted with zinc phosphate cement. Forty-eight bovine incisor roots were selected, endodontically treated, and divided into four groups (n = 12): GA, control (without finishing); GB, GC, and GD, subjected to finishing at 20 minutes, 60 minutes, and 24 hours after cementation, respectively. Root canals were molded, and the resin patterns were cast in copper-aluminum alloy. Cast posts-and-cores were luted with zinc phosphate cement, and the core-finishing procedures were applied according to the groups. The tensile tests were performed at a crosshead speed of 0.5 mm/min for all groups, 24 hours after the core-finishing procedures. The data were subjected to one-way analysis of variance (ANOVA) and Tukey's test (α = 0.05). No significant differences were observed in the tensile strengths between the control and experimental groups, regardless of the time interval that elapsed between the luting and finishing steps. Within the limitations of the present study, it was demonstrated that the core-finishing procedures and time intervals that elapsed after luting did not appear to affect the retention of cast posts-and-cores when zinc phosphate cement was used.